PROPERTIES | ASTM METHOD | SPECIFICATION | TYPICAL | ||||
TURBOLUBE 32 | TURBOLUBE 46 | TURBOLUBE 68 | TURBOLUBE 100 | TURBOLUBE 220 | |||
Viscosity kin. @ 40ºC | D 445 | VG±10% | 32.07 | 46.44 | 68.29 | 94.90 | 212.20 |
Viscosity kin. @ 100ºC | D 445 | VG±10% | - | - | - | - | 18.30 |
Viscosity Index | D 2270 | Min. 100/97/95/95 | 121 | 111 | 104 | 102 | 95 |
Flash Point, ºC | D 92 | Min. 200 | 225 | 228 | 234 | 234 | 288 |
Pour Point, ºC | D 97 | Max. -6 | -12 | -12 | -12 | -12 | -9 |
TAN, mg KOH/g | D 974 | Max. 0.2 | 0.103 | 0.103 | 0.103 | 0.103 | - |
Calcium, ppm | D 4951 | Max. 1 | 0.19 | 0.19 | 0.19 | 0.19 | - |
Zinc, ppm | D 4951 | Max. 1 | 0.24 | 0.24 | 0.24 | 0.24 | - |
CopperStrip Corrosion 3 hours @ 100ºC | D 130 | Max. 1 | ASTM No.1 | ASTM No.1 | ASTM No.1 | ASTM No.1 | ASTM No.1 |
Rust Protection | BS 489 App. A | No Rust | Pass | Pass | Pass | Pass | Pass |
Water Separability @ 54ºC | D 1401 | Max. 40/37/3 (30) | 40/40/0 (25) | 40/40/0 (25) | 40/40/0 (25) | 40/40/0 (25) | 42/38/0 (30) |
Demulsibility | IP 19 | Max. 300/300/360/360 | 240 | 210 | 285 | 300 | - |
Foam Tend./Stab. | D 892 | Max. 65/0 50/0 65/0 | 30/0 20/0 30/0 | 30/0 10/0 30/0 | 20/0 10/0 20/0 | 20/0 10/0 20/0 | 10/0 10/0 10/0 |
Oxidation stab. | IP 280 | ||||||
Total Ox. Prod. %wt Total Sludge %wt |
Max. 0.7/0.8/0.8/0.8 Max. 0.3/0.35/0.35/0.35 |
0.17 0.07 |
0.17 0.07 |
0.17 0.06 |
0.17 0.07 |
- - |
|
Oxidation Life, hr | D 943 | Min. 2000 | 10072 | 10072 | 10072 | 6902 | -20.83 |
FZG, Fail Load Stage, min | D 5182 | Min. 8 | 9 | 9 | 9 | 9 | - |
Carbon Residue, % wt | D 524 | Max. 0.10 | 0.05 | 0.05 | 0.05 | 0.05 | - |
R BOT, minutes | D 2272 | Min. 500 | 1336 | 1336 | 1332 | 1328 | 441 |
R BOT modified, minutes | D 2272 | Min. 80% of time in modified | 1314 | 1314 | 1283 | 1252 | - |
PROPERTIES | ASTM METHOD | SPECIFICATION | TYPICAL | ||||
TURBOLUBE 32 | TURBOLUBE 46 | TURBOLUBE 68 | TURBOLUBE 100 | TURBOLUBE 220 | |||
Viscosity kin. @ 40ºC | D 445 | VG±10% | 32.07 | 46.44 | 68.29 | 94.90 | 212.20 |
Viscosity kin. @ 100ºC | D 445 | VG±10% | - | - | - | - | 18.30 |
Viscosity Index | D 2270 | Min. 100/97/95/95 | 121 | 111 | 104 | 102 | 95 |
Flash Point, ºC | D 92 | Min. 200 | 225 | 228 | 234 | 234 | 288 |
Pour Point, ºC | D 97 | Max. -6 | -12 | -12 | -12 | -12 | -9 |
TAN, mg KOH/g | D 974 | Max. 0.2 | 0.103 | 0.103 | 0.103 | 0.103 | - |
Calcium, ppm | D 4951 | Max. 1 | 0.19 | 0.19 | 0.19 | 0.19 | - |
Zinc, ppm | D 4951 | Max. 1 | 0.24 | 0.24 | 0.24 | 0.24 | - |
CopperStrip Corrosion 3 hours @ 100ºC | D 130 | Max. 1 | ASTM No.1 | ASTM No.1 | ASTM No.1 | ASTM No.1 | ASTM No.1 |
Rust Protection | BS 489 App. A | No Rust | Pass | Pass | Pass | Pass | Pass |
Water Separability @ 54ºC | D 1401 | Max. 40/37/3 (30) | 40/40/0 (25) | 40/40/0 (25) | 40/40/0 (25) | 40/40/0 (25) | 42/38/0 (30) |
Demulsibility | IP 19 | Max. 300/300/360/360 | 240 | 210 | 285 | 300 | - |
Foam Tend./Stab. | D 892 | Max. 65/0 50/0 65/0 | 30/0 20/0 30/0 | 30/0 10/0 30/0 | 20/0 10/0 20/0 | 20/0 10/0 20/0 | 10/0 10/0 10/0 |
Oxidation stab. | IP 280 | ||||||
Total Ox. Prod. %wt Total Sludge %wt |
Max. 0.7/0.8/0.8/0.8 Max. 0.3/0.35/0.35/0.35 |
0.17 0.07 |
0.17 0.07 |
0.17 0.06 |
0.17 0.07 |
- - |
|
Oxidation Life, hr | D 943 | Min. 2000 | 10072 | 10072 | 10072 | 6902 | -20.83 |
FZG, Fail Load Stage, min | D 5182 | Min. 8 | 9 | 9 | 9 | 9 | - |
Carbon Residue, % wt | D 524 | Max. 0.10 | 0.05 | 0.05 | 0.05 | 0.05 | - |
R BOT, minutes | D 2272 | Min. 500 | 1336 | 1336 | 1332 | 1328 | 441 |
R BOT modified, minutes | D 2272 | Min. 80% of time in modified | 1314 | 1314 | 1283 | 1252 | - |
|